Shanghai Unique Alloy Co.Ltd
Focus on Copper Alloy
Casting Tin Bronze C91300
Chemical Composition
Element | |||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
Cu(1,2) | Pb | Sn | Zn | Fe | P(3) | Ni(4) | Al | S | Sb | Si | |
(1) Cu + Sum of Named Elements 99.4% min.(2) In determining Cu min., Cu may be calculated as Cu + Ni.(3) For continuous castings P shall be 1.5% max.(4) Ni value includes Co. | |||||||||||
Min (%) | 79.0 | 18.0 | |||||||||
Max (%) | 82.0 | 0.25 | 20.0 | 0.25 | 0.25 | 1.0 | 0.50 | 0.005 | 0.05 | 0.20 | 0.005 |
Mechanical Properties*
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Compression Deformation Limit (ksi) |
Brinell Hardness, 3000 kg load | ||
---|---|---|---|---|---|---|---|---|---|
As Continuous Cast | 160 Min for Standard | ||||||||
As Sand Cast | As Sand Cast | M01 | 35 Typ | 30 Typ | 0.5 Typ | 24 Min for Standard | 170 Typ | ||
* Measured at room temperature, 68°F (20°C). |
Physical Properties
Melting Point - Liquidus°F | 1632 |
---|---|
Melting Point - Solidus°F | 1505 |
Electrical Conductivity% IACS at 68°F | 7 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi | 16000 |
- Beryllium Copper ꁕ
- Zirconium Copper
- Nickel Silicon Copper ꁕ
- RWMA Copper Alloy ꁕ
- Dispersion strengthened copper ꁕ
- High Copper Alloy
- Silicon Bronze ꁕ
- Phosphor Bronze ꁕ
- Aluminum Bronze ꁕ
- Leaded Nickel Copper ꁕ
- Cadmium Copper
- Silicon brass ꁕ
- Copper Nickel Tin Alloy ꁕ
- Casting Copper Alloy
- Leaded Copper
- Naval Brass ꁕ
- Leaded Commercial Bronze ꁕ
- Manganese Bronze ꁕ
- Iron Copper Alloy ꁕ
- Special Copper Alloy ꁕ
- Free Machining Copper Alloy ꁕ
- EN Wrought Copper Alloy
- JIS Wrought Copper Alloy ꁕ
- Copper Foil ꁕ
- Copper Nickel Alloy
- Copper Nickel Zinc Alloy ꁕ
- Tungsten Copper
- Brass Tube